Improper temperature and humidity degrade core materials (SAP, adhesive), cause adhesive failure, and risk contamination from damaged packaging.
Parameterized Evidence:
Storage Conditions: Products should be stored in a clean warehouse below 35°C and 70% Relative Humidity. SAP's absorption ratio decreases notably with higher ambient humidity; storage at 80% RH for 30 days may reduce the ratio by 15-20% (depending on packaging barrier properties).
Packaging Integrity Standard: The seal strength of individual product packaging (PE pouch) should be ≥1.5N/15mm, with a Water Vapor Transmission Rate (WVTR) ≤5 g/(m²·24h) (at 38°C, 90% RH) to effectively block moisture.
Transportation Testing: Shipping containers should pass transit tests like ISTA 1A, simulating vibration and drop impacts to ensure the product inside does not deform, and adhesive does not contaminate the packaging.
Improper temperature and humidity degrade core materials (SAP, adhesive), cause adhesive failure, and risk contamination from damaged packaging.
Parameterized Evidence:
Storage Conditions: Products should be stored in a clean warehouse below 35°C and 70% Relative Humidity. SAP's absorption ratio decreases notably with higher ambient humidity; storage at 80% RH for 30 days may reduce the ratio by 15-20% (depending on packaging barrier properties).
Packaging Integrity Standard: The seal strength of individual product packaging (PE pouch) should be ≥1.5N/15mm, with a Water Vapor Transmission Rate (WVTR) ≤5 g/(m²·24h) (at 38°C, 90% RH) to effectively block moisture.
Transportation Testing: Shipping containers should pass transit tests like ISTA 1A, simulating vibration and drop impacts to ensure the product inside does not deform, and adhesive does not contaminate the packaging.
ที่อยู่
ร้านค้าที่ 5 อาคาร 12 สวนฟูฮาโอ ถนนอันซิน 1st ถนนกิเชง เขตนานไฮ เมืองโฟชาน จังหวัดกวางดง
โทรศัพท์
86--1392545435
อีเมล
susannayee0205@gmail.com
english
français
Deutsch
Italiano
Русский
Español
português
Nederlandse
ελληνικά
日本語
한국
polski
فارسی
বাংলা
ไทย
tiếng Việt
العربية
हिन्दी
Türkçe
indonesia